Controlling heterogeneous nucleation and growth of foams

ABSTRACT

A method of controlling the nucleation of cells in a polymeric foam material includes blending a matrix material with a second phase material which provides sites for bubble nucleation. The selection of the second phase material controls the size and density of the cells.

FIELD OF THE INVENTION

This invention relates to controlling the cell size of foams, and more particularly, to using a matrix polymeric material with a second phase material which provides sites for bubble nucleation within the matrix of the polymeric material to produce controlled cell size in microcellular foams.

BACKGROUND OF THE INVENTION

Microcellular foams for use in packaging, containers, films, and the like have been reported. See U.S. Pat. No. 4,473,665-Martini-Vredensky, Suh and Waldman; U.S. Pat. No. 4,761,256-Hardenbrook, et al; and Ph.D. Thesis, MIT 1986, Jonathan Colton. In this prior art, small cell size is obtained by quenching the material during the formation of the cells at the appropriate time to control the size of the cells.

Various methods of density reduction have been investigated. These approaches cause a nearly linear property reduction with bulk density. These techniques typically use a chemical blowing agent (CBA) to create foam structure in polyethylene. Most used two or three layer coextrusions with foam comprising the "core". The best material made using this approach still has significant property degradation with density reduction. However, the data shows that as cell size decreases and cell uniformity increases film properties suffer far less. This suggests that very fine, well controlled cells could reduce bulk density while retaining acceptable properties.

Recently several articles have disclosed research into very fine cell foams or microfoams, with cells between 3 and 10 microns. This shows the interesting result that microcells improve rather than decrease impact properties of plaque molded samples. These small foam cells prevent crack growth in the matrix by dissipating the force at the crack tip over a much wider area similar to the effect of rubber particles in high impact polystyrene (HIPS). Typical cell sizes for "fine cell" styrene foams are 100+ microns and, although they have better impact properties than coarser foam structures, they are poorer than the styrene matrix. Microfoaming creates an impact resistant structure that has better properties than the unreduced matrix.

The method reported in the literature to create a microcellular foam is to add a material to the molten polymer at its solubility limit at the polymer melt temperature. This material is molded into a plaque sample and rapidly quenched. Plaques are put into a Paar bomb and saturated with a gas (nitrogen, carbon dioxide) at elevated pressures for times sufficient to ensure gas diffusion into the polymer matrix. Samples are then quickly heated to reduce matrix viscosity, increase gas volatility in the matrix and create micro foam. A material added at its solubility limit will supposedly create nucleating sites for foam cells as the molten polymer cools and the material precipitates from solution. Since the material is soluble and hence uniformly distributed, the nucleation sites are uniformly distributed throughout the matrix. The site size is very small since the nucleation occurs on the forming precipitate which can be clumps as small as several molecules. This nucleation mechanism has been referred to as "pseudo-homogeneous" since the effect of the added material as a typical nucleant is unclear. Zinc stearate and stearic acid have been used as nucleants in this manner.

Much of the work recently reported in the literature originated at MIT and Dr. Nam Suh. Several theses were published (The Production and Analysis of Microcellular Foam, J. E. Martini, MS thesis, 1981; The Processing of Microcellular Foam, F. A. Waldman, MS thesis, 1980; The Nucleation of Microcellular Thermoplastic Foam, PhD thesis, 1985) and later reported in various journal articles. The aforementioned U.S. Pat. No. 4,473,665 titled "Microcellular Closed Cell Foams and Their Method of Manufacture; Saturation With Inert Gas, Depressurization and Quick-Cooling" is a process patent describing the microfoam method. Microfoam work at MIT spans about ten years and includes work in both crystalline as well as amorphous polymers. The bulk of the work reported has been in various styrene matrices due to processing ease and subsequent characterization.

Polycarbonate foams, polyetherimide (Ultem®) foams, polypropylene oxide/polystyrene or HIPS foams, Noryl®, are also in use. See, for example, U.S. Pat. No. 4,598,101.

SUMMARY OF THE INVENTION

Controlled foaming of amorphous crystalline polymers such as polystyrene, polyphenylene oxide polystyrene, polyetherimide, polycarbonate, polyethylene, polypropylene, nylon, teflon, and other polymers can be achieved by blending them with a second phase material which has a transition temperature below that of the polymer. This provides sites which can be activated for bubble nucleation. As used herein, "transition temperature" includes the glass transition temperature or the melting point of the crystalline polymer. The number of sites per unit volume of unfoamed resin is controlled by the volume fraction of the second phase material, the degree of dispersion of this phase and the extent of activation of these sites as bubble nuclei.

As an example, HIPS is incorporated into a crystalline resin. The second phase and the density and size of the rubber particles implanted from the HIPS determines the number of activatable bubble nucleation sites. The number of bubbles per unit volume of unfoamed resin approximates the number of activatable rubber particles. The rubber particles act as bubble nuclei if they are stressed sufficiently so as to cavitate at the boundary between the rubber particle and the polymer matrix, within the rubbery particle, or at the interface between the rubber and the occluded styrene particles. These separate interfaces can be activated by cooling to a sufficiently low temperature, by rapid quenching, and by shear when the matrix is incapable of sufficiently rapid response to stress. The particles can be mixed with surfactants which make the cavitation at the rubber particle interfaces easier. The foaming of the resin can be accomplished with either a supersaturated gas forming species or liquid blowing agent.

SHORT DESCRIPTION OF THE DRAWINGS

FIG. 1 is a schematic diagram of a model cell depicting the nucleation and formation of the cell;

FIG. 2 depicts the apparatus and process that was used to produce the microcellular foams of the examples;

FIG. 3 is a drawing representing the foams produced from polyphenylene oxide and HIPS;

FIG. 4 is a drawing representing the foams produced in a manner similar to that of FIG. 3;

FIG. 5 is a drawing representing the foam produced with raw HIPS with no second phase material added;

FIG. 6 includes graphs depicting the independence of cell size to process pressure;

FIG. 7 includes graphs showing the independence of cell size to process temperature; and

FIG. 8 includes graphs showing cell size as a function of the rubber particle size.

DESCRIPTION OF THE PREFERRED EMBODIMENT

FIG. 1 is a schematic diagram of a model of the cell formation in a polymer matrix of the present invention. A polymeric matrix material 11 has cells 12 which are formed by a second phase polymeric material 13. The second phase material has a glass transition or melting temperature below the transition temperature of the polymeric matrix material 11. As the composition is heated and cooled, the second phase material nucleates a cell. As the composition is heated and cooled, the transition temperature of both the matrix material and the second phase material is exceeded. As the composition is cooled, the matrix material goes through its transition temperature. Now there is a marked difference in the thermal expansion coefficient between the matrix material and the second phase material. The matrix material shrinks much slower (for example, five times slower) than the second phase material. This puts tensile stress on the interface. This stress produces a void which ultimately becomes a cell. Gas under pressure, depicted by the arrows 14, enters the cell 12 and it expands. The expansion of the cell is limited by the physical size of the particle in the second phase material. The outer limits of this matrix are depicted by the circle 15 which is at the boundary between the polymeric material 11 and the second phase material 13. Second phase material 13 is originally present in the matrix as a discrete nucleating particle prior to development of cell 12. The size of these discrete particles is from 0.02 to 10 microns.

Elastomers, particularly rubber particles, are particularly suitable second phase materials. Rubber in high impact polystyrene or in latex has been successfully used as a nucleating agent. HIPS is a source of rubber particles which can be compounded into almost any polymer at 0.1 to 10% and not substantially change the base polymer properties. Rubber latex is a rubber/liquid, water based emulsion.

Examples of compositions including matrix material and second phase material which have the requisite transition temperatures are:

    ______________________________________                                         MATRIX MATERIAL SECOND PHASE MATERIAL                                          ______________________________________                                         Polystyrene     Rubber                                                         Polycarbonate   Rubber                                                         Polyester       Rubber                                                         Polyethylene    Rubber                                                         Polyethylene    Polystyrene                                                    Polyetherimide  Polypropylene                                                  Polyetherimide  Polyethylene                                                   Polyphenylene oxide/                                                                           Rubber                                                         polystyrene                                                                    ______________________________________                                    

Polyetherimide is sold under the trade name Noryl® by the General Electric Company. Polyphenylene oxide/polystyrene is sold under the trade name Ultem® by the General Electric Company.

FIG. 2 depicts the apparatus which produced the compositions of the examples. FIG. 2 also depicts the process for producing the compositions of the present invention.

Extruder 19 compounds the polymeric matrix material and the second phase material to produce samples. During extrusion, the material is above the transition temperature of the matrix material. Merely cooling below the matrix transition temperature is sufficient to activate the cell nucleation process. A sample 20 is placed in pressure vessel 21 where the sample is impregnated with gas at an elevated pressure, for example, from the nitrogen cylinder 22. Any gas can be used, including nitrogen, carbon dioxide, helium, argon, and NO_(x). These can be combined with conventional blowing agents such as CFCs, carbon dioxide, methylene chloride, pentane, etc. Anything that is soluble in the second phase material (rubber) and which has a vapor pressure substantially above the ambient pressure during the foam nucleation and expansion at temperature is suitable for use.

The gas impregnated samples are heated in the high temperature bath 23 to foam them. The samples are then slowly cooled to room temperature. The samples may then be quenched in the liquid nitrogen flask 24 and fractured to expose the foam cells. It has been found that rapid quenching is not necessary for the samples produced with HIPS or latex as the second phase material.

A scanning electron microscope 25 was used to produce photo micrographs of the foamed samples and a computer system 26 was used for cell size analysis.

EXAMPLES

The polymer samples were blended using two procedures. The first procedure utilized a twin screw extruder. The second procedure used a laboratory rheomex single screw extruder with a 1" barrel and a dc drive control system which gave variable speeds from 0 to 250 rpm. The extruder was equipped with a right angle die and a capillary such that the extrudate was extruded at a diameter of 3/32" . For all of the materials that were compounded, the extruder was operated at the maximum shear rate (rotation speed of the screw) that could be tolerated without exceeding the limitations of the pressure disk that was attached to the extruder. The extrudate was cooled in air or a hot water bath and pelletized using a laboratory pelletizer. The resulting pellets were then in some cases remixed and reextruded to provide a double pass through the extruder to improve the dispersion.

The different polymer samples were loaded in a Parr autoclave. The autoclave was then sealed and nitrogen gas was administrated into the autoclave at a pressure up to 2,000 pounds per square inch. The samples were then left in the autoclave for up to 7 days to obtain permeation of the nitrogen gas into the polymeric materials. The materials were then removed from the autoclave and subjected to a heat flux environment of a hot oil bath, microwave oven, or a convective hot air oven at different temperatures. The foaming characteristics of the materials were observed during the heating. The foams were removed from the high temperature, allowed to cool slowly to room temperature, and stored at room temperature until they were analyzed. The foamed materials and the precursors were then evaluated using scanning electron microscopy to determine the degree of dispersion of the second phase nucleation agent and the type and consistency of the microcellular foam that was produced.

Foams nucleated with rubber latex and HIPS were produced by nitrogen saturation of an LLDPE dispersion at about 2,000 psi pressure and subsequent heating in an oil bath or a convective oven.

Example 1

Latex was allowed to dry on linear low density polyethyelene (LLDPE) pellets in order to facilitate the addition of the mixture in the extruder. The rubber latex was compounded in the LLDPE using a single screw bench top extruder running at maximum rpm. The materials were extruded into a water bath. The extrudate was cooled and cut into pieces. Nitrogen gas was permeated into the linear low density polyethylene (LLDPE)/latex pieces under pressure (up to 2,000 psi). The pieces were removed from the pressure and heated. When heated, foaming occurred. The original latex had approximately 0.1 micron diameter particles and electron microscopy indicates that the final particle size in the dispersion ranges from 0.5 to 1.2 microns. The LLDPE/latex blends were foamed at approximately 165° C. in a convective hot air oven. Foams were produced with bubble diameters between 10 and 100 microns depending upon the heat flux during foaming.

Example 2

A foamable material was blended using the same single screw extruder with 20 to 40 volume percent of HIPS in LLDPE. Foams were produced with cell sizes in the neighborhood of 10 micron in diameter.

Example 3

Noryl® material (General Electric) with a 1:1 weight ratio of polypropylene oxide (PPO)/HIPS was microcellularly foamed using the above procedures. This composition has about 15 volume percent rubbery particles. The temperature of the foaming was 165° C. The material foamed well as demonstrated in FIG. 3.

Example 4

Foams are produced from polystyrene blended with polymer having rubber with particle size of 250 angstroms. These rubber particles are the glass transition phase of a block copolymer. The polymer was saturated at 13.8 MPa with nitrogen and foamed in an ethylene glycol bath. The cell size is greater than 10 microns. This same material was compounded into polystyrene, a typical amorphous polymer, so that the rubber particles were approximately 10⁸ per cubic centimeter of unfoamed resin. The material was treated in the same way. It was saturated at 13.8 megapascals and it was heated to approximately 388° K. FIG. 4 is a drawing representing the resultant material with cell sizes in the 3-5 micron range.

Example 5

High impact polystyrene, with a particle size of about 2 microns and about 30 volume percent rubbery particles (hereafter identified as HIPS 5400) was subjected to the same foaming conditions as previously given. It was heated to approximately 115° C. at 2,000 psi. FIG. 5 is a drawing representing the foamed material. Note that the cells produced had a size in excess of 30 microns.

Example 6

Linear low density polyethylene, LLDPE, a typical semi-crystalline polymer, was foamed with HIPS 5400, HIPS 7800 (0.8 micron particle size) with a nominal molecular weight of 200,000 and crystalline polystyrene identified as (PS 1500) as second phase materials, following the process conditions described above. HIPS 5400 has a typical salami type rubber particle with many small particles of polystyrene in each rubber particle. The average rubbery particle size of 5400 is about 2 microns. HIPS 7800 has core shell rubber particles of about 0.8 microns. PS 1500 is pure polystyrene. These materials were compounded into the LLDPE using a twin screw extruder at concentrations from 2.0 to 18 volume percent. Data showing cell size supports the conclusion that the addition of materials with a transition temperature below that of the matrix polymer nucleates a foam and leads to controlled foaming. The data show that the density goes down with increased saturation pressure. For example, using a one melt index LLDPE and HIPS with a particle size of 0.8 microns the density went from 0.94 to 0.53 as the pressure is increased from 0 to 2,000 psi. As the number of particles activated are increased, the density increases because the gas is distributed over more cells.

Example 7

Several experiments were performed to demonstrate the effect of process pressure, process temperature, and rubbery particle size on foam cell size. The results are presented in FIGS. 6, 7, and 8.

FIG. 6 is a graph showing cell size as a function of process pressure for several samples. The circles depict samples of polystyrene without second phase material and the rectangles depict the same polystyrene with HIPS added. The samples which include the second phase polymeric material with a lower transition temperature demonstrate minimal dependence of cell size to process pressure. On the other hand, the samples produced under the same process conditions, but without second phase material being added, demonstrate a strong dependence on process pressure.

FIG. 7 shows graphs of cell size versus process temperature for various samples with and without a second phase material being added. The samples depicted by rectangles are compositions which include a second phase material having a transition temperature below that of the matrix material. These samples show minimal dependence of cell size for various process temperatures. The samples without the added second phase, which were processed under similar conditions, show a strong dependence of cell size on process temperature.

FIG. 8 shows the influence of rubber particle size on cell size. Cell size as a function of the particle size is depicted for various process pressures. This demonstrates that the cell size can be selected by selecting the proper nucleating particle to be included as the second phase material.

Examination of the fracture surfaces of these foams produced using the second phase materials and using oxygen plasma demonstrated that the second phase was substantially distributed over the interior surface of the cells. This material controls the growth of the cells.

Example 8

An amorphous polymer matrix with about 0.3 percent rubber particles was saturated with nitrogen, plasticated in an extrusion device, and injected into a mold. The foamed polymer entered the room temperature mold at an approximate temperature of 165° C. The part had a fine, about 10 micron, cell size and a substantially lower density than a pure polystyrene produced under similar conditions.

Example 9

Pure polystyrene was saturated with nitrogen at an elevated pressure and extruded using a single screw extruder fitted with a capillary die at 165°. The resulting foam cells had a broad distribution with an average cell size well above the desired 10 micron size. The experiment was repeated while adding 0.3 percent rubber particles to the polystyrene. The resulting foam rod was slowly cooled in the ambient air and it had a narrow cell size distribution with an average size of about 10 microns.

Example 10

Polystyrene was saturated at room temperature with carbon dioxide. It was then heated in a microwave oven. It produced large nonuniform cells. The same experiment was performed using polystyrene with 0.03 percent rubbery second phase. The resulting foam had cells of about 10 micron size and produced parts suitable for use in transport of fragile equipment.

While particular embodiments of the invention have been shown and described, various modifications are within the true spirit and scope of the invention. The appended claims are, therefore, intended to cover all such modifications. 

What is claimed is:
 1. A method for producing closed cell foamed structures, comprising:blending a polymeric matrix material with a second phase material which has a transition temperature below that of said polymeric matrix material to form an unfoamed composition, said second phase material being present in said unfoamed composition in a concentration between 0.001 and 18 volume percent; heating said unfoamed composition to a temperature above the transition temperature of the matrix material; cooling said unfoamed composition to a temperature below the transition temperature of the polymeric matrix material to provide sites which can be activated for bubble nucleation, whereby said sites are provided by voids resulting from stresses caused by differing thermal expansion coefficients between the second phase material and the polymeric phase material; impregnating said unfoamed composition with gas at an elevated pressure; and heating said impregnated unfoamed composition to expand cells at said sites to form a foamed structure.
 2. The method recited in claim 1 further comprising:selecting said second phase material to limit the expansion of said cells by the physical size of the particles in said second phase material.
 3. The method recited in claim 1 further comprising:controlling the density of cells in said foamed structures by adjusting the amount of said second phase material added to said matrix material during blending.
 4. The method recited in claim 1 wherein said second phase polymeric material has particles of rubber which act as nucleation sites.
 5. The method recited in claim 1 wherein said second phase material is high impact polystyrene.
 6. The method recited in claim 1 wherein said second phase material is latex.
 7. The method recited in claim 1 wherein said matrix material is an amorphous polymer.
 8. The method recited in claim 1 wherein said matrix material is an amorphous polymer and said second phase material is an amorphous polymer.
 9. The method recited in claim 1 wherein said polymeric matrix material is polystyrene and said second phase material is rubber.
 10. The method recited in claim 1 wherein said polymeric matrix material is polycarbonate and said second phase material is rubber.
 11. The method recited in claim 1 wherein said polymeric matrix material is polyester and said second phase material is rubber.
 12. The method recited in claim 1 wherein said polymeric matrix material is polyethylene and said second phase material is rubber.
 13. The method recited in claim 4 wherein said foamed structures are microcellular.
 14. The method recited in claim 1 wherein said polymeric matrix material is polyetherimide and said second phase material is rubber.
 15. The method recited in claim 4 wherein said matrix material is polyphenylene oxide/polystyrene.
 16. The method recited in claim 1 wherein said polymeric matrix material is polyethylene oxide/polystyrene and said second phase material is rubber.
 17. The method recited in claim 4 wherein said polymeric matrix material is semicrystalline polymer.
 18. The method recited in claim 1 wherein said matrix material is semicrystalline polymer and said second phase material is an amorphous polymer.
 19. The method recited in claim 1 wherein said matrix material is semicrystalline polymer and said second phase material is an semicrystalline polymer.
 20. The method recited in claim 1 wherein said matrix material is an amorphous polymer and said second phase material is a semicrystalline polymer.
 21. The method of claim 4 wherein said polymeric matrix material is selected from the group consisting of polyester, polyethylene, polystyrene acrylo nitril, polyphenylene oxide/polystyrene, polycarbonate, polyetherimide, polypropylene, nylon, and teflon.
 22. The method of claim 1 further comprising cooling said foamed structure to about room temperature, provided that said cooling does not encompass quenching.
 23. The method of claim 1 wherein the particle size of the second phase material is from 0.02 to 10 microns.
 24. The method of claim 23 wherein said second phase material comprises high impact polystyrene.
 25. The method of claim 23 wherein said second phase material comprises rubber.
 26. The method of claim 23 wherein said polymeric matrix material comprises polystyrene and said second phase material comprises rubber.
 27. A method of producing foamed structures with predictable cell size and density, comprising:blending a polymeric matrix material selected from the group consisting of polyester, polyethylene, polystyrene acrylo nitril, polyphenylene oxide/polystyrene, polycarbonate, polyetherimide, polypropylene, nylon and teflon with a second phase material having a lower transition temperature than said matrix material, said second phase material being present in said blend at a concentration of from 0.001 to 18 volume percent of said blend; heating said blend to a temperature above the transition temperature of the matrix material; cooling said heated blend to a temperature below the transition temperature of the polymeric matrix material to provide sites which can be activated for bubble nucleation, whereby said sites are provided by voids resulting from stresses caused by differing thermal expansion coefficients between the second phase material and the polymeric matrix material; impregnating said blend with gas at an elevated pressure; and heating said impregnated blend to expand cells at said sites to form a foamed structure.
 28. The method recited in claim 27 wherein the expanded cell size is less than 10 microns.
 29. The method recited in claim 27 wherein said matrix material is amorphous and said second phase material includes rubber particles.
 30. The method recited in claim 27 wherein said matrix material is amorphous and said second phase material is high impact polystyrene.
 31. The method recited in claim 27 wherein said matrix material is semicrystalline and said second phase material includes rubber.
 32. The method recited in claim 27 wherein said matrix material is semicrystalline and said second phase material is high impact polystyrene.
 33. A method of producing foamed structures with predictable cell size and density, comprising:blending a polymeric matrix material with a second phase material to form an unfoamed composition, said second phase material having a preselected particle size and a transition temperature below that of said polymeric matrix material, said second phase material being present in said unfoamed composition at a concentration between 0.001 and 18 volume percent; heating said unfoamed composition to a temperature above the transition temperature of the matrix material; cooling said heated unfoamed composition to a temperature below the transition temperature of the polymeric matrix material to provide sites which can be activated for bubble nucleation, whereby said sites are provided by voids resulting from stresses caused by differing thermal expansion coefficients between the second phase material and the polymeric matrix material; impregnating said unfoamed composition with gas at an elevated pressure; reducing said process pressure; and heating said impregnated material to a process temperature to expand said cells to a size dependent on the particle size of the second phase material, thereby foaming the material.
 34. The method of claim 33 wherein said second phase material comprises rubber.
 35. The method of claim 34 further comprising blending said matrix material and said second phase material at a temperature above the transition temperature of the matrix material.
 36. The method of claim 34 further comprising selecting the particle size of said second phase material to provide a predetermined size of said cells.
 37. The method of claim 36 wherein said polymeric matrix material comprises polystyrene.
 38. The method of claim 34 wherein said polymeric matrix material is selected from the group consisting of polyester, polyethylene, polystyrene acrylo nitril, polyphenylene oxide/polystyrene, polycarbonate, polyetherimide, polypropylene, nylon, and teflon.
 39. A method for producing a microcellular foamed polymer composition comprising:(a) providing a matrix polymeric material; (b) blending a second phase material having a particle size of from 0.02 to 10 microns and having a transition temperature below the transition temperature of said matrix polymeric material with said matrix polymeric material to form an unfoamed composition, said second phase material being present in an amount of from 0.001 to 18 volume percent of said unfoamed composition; (c) heating said unfoamed composition to a temperature above the transition temperature of the matrix polymeric material; (d) cooling said heated unfoamed composition to a temperature below the transition temperature of the matrix polymeric material to provide sites that can be activated for bubble nucleation, whereby said sites are provided by voids resulting from stresses caused by differing thermal expansion coefficients between the second phase material and the matrix polymeric material; (e) impregnating said cooled unfoamed composition with a gas at an elevated pressure; and (f) heating said impregnated unfoamed composition to expand cells at said sites to form the foamed polymer composition.
 40. The method of claim 39 wherein the average size of the expanded cells is below about 40 microns.
 41. The method of claim 39 wherein the average size of the expanded cells is below about 10 microns.
 42. The method of claim 41 wherein the matrix polymeric material comprises polystyrene.
 43. The method of claim 42 wherein the second phase material comprises rubber in an amount of from 0.1-10% by volume of the unfoamed matrix composition.
 44. The method of claim 41 wherein the matrix polymeric material is selected from the group consisting of polyester, polyethylene, polystyrene acrylo nitril, polyphenylene oxide/polystyrene, polycarbonate, polyetherimide, polypropylene, nylon, and teflon. 